BITUMEN GRADE 85/100

NO	Test	Acceptable Range	Test Method
1	PENETRATION @250C,0.1 MM	85/100	ASTM D5/2013
2	SOFTENING POINT (R&B), 0C	42 min	ASTM D36/2012
3	DUCTILITY, 250C, 5CM/MIN, Cm	> 100	ASTM D113/2007
4	SPOT TEST	NEG	A.A.S.H.T.O T102-09
5	FLASH POINT, (0C)	232min	ASTM D92/2013
6	SOLUBILITY IN TCE, %WT	99.0min	ASTM D2042/2009
7	DENSITY @ 150C	-	ASTM D70/2009
8	LOSS ON HEATING, Mass%	1 max	ASTM D6/2011
9	DROP IN PENETRATION %	20 Max	ASTM D6 & D5

BITUMEN GRADE 60/70

NO	Test	Acceptable Range	Test Method
1	PENETRATION @250C,0.1 MM	60/70	ASTM D5/2013
2	SOFTENING POINT (R&B), 0C	46 min	ASTM D36/2012
3	DUCTILITY, 250C, 5CM/MIN, Cm	>100	ASTM D113/2007
4	SPOT TEST	NEG	A.A.S.H.T.O T102-09
5	FLASH POINT, (0C)	230 min	ASTM D92/2013
6	SOLUBILITY IN TCE, %WT	99.0 min	ASTM D2042/2009
7	DENSITY @ 150C	-	ASTM D70/2009
8	LOSS ON HEATING, Mass%	0.8 max	ASTM D6/2011
9	DROP IN PENETRATION %	20 Max	ASTM D6 & D5

BITUMEN GRADE 40/50

NO	Test	Acceptable Range	Test Method
1	PENETRATION @250C,0.1 MM	40/50	ASTM D5/2013
2	SOFTENING POINT (R&B), 0C	49 min	ASTM D36/2012
3	DUCTILITY, 250C, 5CM/MIN, Cm	>100	ASTM D113/2007
4	SPOT TEST	NEG	A.A.S.H.T.O T102-09
5	FLASH POINT, (0C)	232 min	ASTM D92/2013
6	SOLUBILITY IN TCE, %WT	99.0 min	ASTM D2042/2009
7	DENSITY @ 150C	1.01-1.06	ASTM D70/2009
8	LOSS ON HEATING, Mass%	0.8 max	ASTM D6/2011
9	DROP IN PENETRATION %	20 Max	ASTM D6 & D5

UREA SPECIFICATION

NO	PROPERTY	UNITS	TEST METHOD	SPEC Value
01	N2 content	Wt %	BS DIN EN 15478	Min 46
02	Biuret content	Wt %	BS DIN EN 15479	Max 1.0
03	Moisture	Wt %	ISO 760	Max 0.3
04	Particle size (1-2.4 mm)	%	ISO 8397	Min 90
05	Urea Formaldhide (UF)	%	H.F.T 1.6 & SBB 0071-02-E	Max 0.4

AMONYAK SPECIFICATION

NO	PROPERTY	UNITS	TEST METHOD	SPEC Value
01	Purity	Wt%		Min 99.7
02	Oil content	ppm	ISO 7106	Max 5.0
03	Moisture	Wt%	ISO 7105	Max 0.35

CRYSTAL MELAMINE SPECIFICATION

NO	PROPERTY	UNITS	TEST METHOD	SPEC Value
01	Purity	Wt %	JIS K1531	Min 99.8
02	Ash content	Wt %	JIS K1531	Max 0.03
03	Moisture	Wt %	JIS K1531	Max 0.1
04	Color	APHA	JIS K1531	Max 20